聚苯胺长效防腐水性环保涂料的研制及性能研究
2013-06-03 14:07:38
作者：康先进等来源：
摘要：采用原位化学合成法制备对甲苯磺酸掺杂的聚苯胺/二氧化硅复合材料，并用红外光谱、扫描电镜和透射电镜表征其结构，以合成的聚苯胺/二氧化硅为功能组分，丙烯酸水性乳液为成膜物质，制成水性环保防腐涂料。用电化学测试技术研究复合水性防腐涂料对碳钢基材的防护效果。结果表明，复合水性防腐涂料使金属基体的腐蚀电位正移，具有较好的钝化效果,增强了耐蚀性。
Absract：Polyaniline-SiO2 was in situ synthesized and doped by p-toluenesulfonic acid (p-TSA). The composites were characterized by FTIR, SEM and TEM. The corrosion performance of polyaniline-SiO2 pigmented waterborne coating on carbon steel was studied by electrochemical testing technique in 3.5% NaCl solution. The tested results showed that a passivation effect and a positive shift of corrosion potential occurred due to the application of coating on metals and the anticorrosion property was enhanced.
Key Word：polyaniline ,SiO2,waterborne coating,polarization
Absract：Polyaniline-SiO2 was in situ synthesized and doped by p-toluenesulfonic acid (p-TSA). The composites were characterized by FTIR, SEM and TEM. The corrosion performance of polyaniline-SiO2 pigmented waterborne coating on carbon steel was studied by electrochemical testing technique in 3.5% NaCl solution. The tested results showed that a passivation effect and a positive shift of corrosion potential occurred due to the application of coating on metals and the anticorrosion property was enhanced.
Key Word：polyaniline ,SiO2,waterborne coating,polarization
相关文章
无相关信息