7A52铝合金干湿交替情况下电偶腐蚀行为研究
2014-08-13 16:16:36 作者:本站整理来源:

王伟  黄燕滨 徐可可

(装甲兵工程学院,北京 100072)

  摘要:本文针对海洋环境下7A52铝合金干湿周浸使用过程中存在的电偶腐蚀现象进行研究,测试了干湿周浸情况下7A52与38CrSi、5A06之间的电偶电流及电偶电压,使用SEM对腐蚀后的表面进行了分析,实验发现,干湿周浸情况下,试样表面腐蚀产物较多且堆积比较松散,试样的腐蚀速度比全浸更加严重。

  关键词:7A52,电偶腐蚀,干湿周浸

  Study on Galvanic Corrosion in Cyclic Wet-dry Immersion Test of 7A52 Aluminium Alloy

  WANG Wei  HUANG Yan-bin XU Ke-ke

  (Academy of Armored Forces Engineering,Beijing 100072;)

  Abstract: In this paper, The galvanic corrosion of 7A52 in after cyclic wet-dry immersion is been studied. We have studied 38CrSi and 5A06 that often been used arrange in pairs or groups with 7A52 .The galvanic current and galvanic voltage of two different materials is been tested. We have studied the surface of samples after corrosion use SEM. We can get that in cyclic wet-dry immersion , the structure of corrosion product is loose and more gap , the corrosion rate is more serious.

  Key words:7A52; galvanic corrosion;cyclic wet-dry immersion test

  联系方式

  徐可可:ly20042089@126.com

关于国家科技资源服务平台

国家科技基础条件平台中心是科技部直属事业单位,致力于推动科技资源优化配置,实现开放共享,其主要职责是:承担国家科技基础条件平台建设项目的过程管理和基础性工作;承担国家科技基础条件平台建设发展战略、规范标准、管理方式、运行状况和问题的研究,以及国际合作与宣传、培训等工作;承担科技基础条件门户系统的建设与运行管理工作;参与对在建和已建国家科技基础条件平台项目的考核评估和运行监督工作。

国家科技资源服务平台相关网站


国家材料腐蚀与防护科学数据中心

国家高能物理科学数据中心

国家基因组科学数据中心

国家微生物科学数据中心

国家空间科学数据中心

国家天文科学数据中心

国家对地观测科学数据中心

国家极地科学数据中心

国家青藏高原科学数据中心

国家生态科学数据中心

国家冰川冻土沙漠科学数据中心

国家计量科学数据中心

国家地球系统科学数据中心

国家人口健康科学数据中心

国家基础学科公共科学数据中心

国家农业科学数据中心

国家林业和草原科学数据中心

国家气象科学数据中心

国家地震科学数据中心

国家海洋科学数据中心