Hastelloy C-22合金是一种通用的镍铬钼合金，密度为8.7g/cm3。与常见的镍铬钼合金，如C-276、C-4、625合金等相比，其具有更好更全面的耐蚀性能。
各国对照
|
中国
|
GB/T 15007-2008
|
NS3308
|
|
美国
|
ASTM B462-2006
ASTM B574-2006
ASTM B575-2006
|
N06022
|
|
Special Metals
|
INCONEL® alloy 22
|
|
Haynes International
|
HASTELLOY® C-22®
|
|
日本
|
JIS H 4551:2000
|
NW6022
|
|
Nippon Yakin
|
NAS NW22
|
|
德国
|
DIN 17744:2002
|
NiCr21Mo14W
2.4602
|
|
VDM Metals
|
VDM® Alloy 22
Nicrofer® 5621 hMoW
|
成分规范
|
牌号
|
NS3308
|
N06022
|
NW6022
|
2.4602
|
|
C
|
≤0.015
|
≤0.015
|
≤0.015
|
≤0.010
|
|
Si
|
≤0.08
|
≤0.08
|
≤0.08
|
≤0.08
|
|
Mn
|
≤0.50
|
≤0.50
|
≤0.50
|
≤0.50
|
|
P
|
≤0.020
|
≤0.020
|
≤0.025
|
≤0.025
|
|
S
|
≤0.020
|
≤0.020
|
≤0.020
|
≤0.015
|
|
Ni
|
余量
|
Remainder
|
残部
|
Other
|
|
Cr
|
20.0~22.5
|
20.0~22.5
|
20.0~22.5
|
20.0~22.5
|
|
Mo
|
12.5~14.5
|
12.5~14.5
|
12.5~14.5
|
12.5~14.5
|
|
Fe
|
2.0~6.0
|
2.0~6.0
|
2.0~6.0
|
2.0~6.0
|
|
W
|
2.5~3.5
|
2.5~3.5
|
2.5~3.5
|
2.5~3.5
|
|
Co
|
≤2.50
|
≤2.50
|
≤2.50
|
≤2.50
|
|
V
|
≤0.35
|
≤0.35
|
≤0.35
|
≤0.35
|
材料特点
① 在氧化和还原条件下，对各种腐蚀性介质均有出色的耐受性；是仅有的几种能够耐潮湿氯气、次氯酸盐以及二氧化氯溶液腐蚀的材料之一，对高浓度的氯化盐溶液具有显著的耐腐蚀性（如氯化铁和氯化铜）。
② 在高达677℃的高温下也能抵抗多种腐蚀环境。
③ 良好的耐点蚀、缝隙腐蚀和应力腐蚀开裂性能。
④ 优异的焊接性能。
应用场合
Hastelloy C-22合金在化工和石化领域得到了广泛的应用，如应用在接触含氯化物有机物的元件和催化系统中。这种材料尤其适合在高温、混有杂质的无机酸和有机酸（如甲酸和乙酸）、海水腐蚀环境中使用。